| 摘要 |
In a known method for producing a raised marking on a glass object, a suspension containing SiO2 particles is applied to a surface of the glass object as a pattern, and the pattern is compacted to form the marking. Starting from this, in order to enable a cost-effective production of an optically appealing and uniform marking on an object made of quartz glass, which marking is also suited for applications at high temperature or in a contamination-sensitive environment, such as in solar cell and semiconductor production, it is suggested according to the invention that a binder-free suspension be used to create a marking on a quartz glass object, the suspension containing a dispersion liquid and amorphous SiO2 particles having particle sizes of up to a maximum of 500μm, of which are between 0.2% by wt. and 15% by wt. SiO2 nanoparticles having particle sizes of less than 100 nm, and the solids content thereof, i.e. the weight proportion of the SiO2 particles and of the SiO2 nanoparticles together, is in the range between 60% and 90%.
|