| 摘要 |
PROBLEM TO BE SOLVED: To provide an antifogging propylene resin sheet having excellent transparency and antifogging characteristics and generating less discoloration when recycling. SOLUTION: A propylene resin sheet is formed by applying 0.05-2 g/m<SP>2</SP>of an antifogging agent in solid content onto at least one side of a propylene resin sheet having a thickness of 0.1-2 mm. The propylene resin sheet includes a propylene resin composition which contains 0.005-0.04 pts.wt. of at least one fatty acid metal salt composed of a 6-22C fatty acid and a metal selected from among calcium, sodium, zinc, lithium, aluminum and magnesium based on 100 pts.wt. of propylene resin which has an MFR of 0.3-20 g/10 min and is obtained using a Ziegler catalyst. The antifogging agent is composed of sucrose fatty acid ester of a 6-22C fatty acid. COPYRIGHT: (C)2011,JPO&INPIT
|