Hot dip galvanized steel sheet excellent in shapeability and plateability comprised of high strength steel sheet according to the present invention can be provided containing, by mass % about, C: 0.05 to 0.25%, Si: 0.3 to 2.5%, Mn: 1.5 to 2.8%, P: 0.03% or less, S: 0.02% or less, Al: 0.005 to 0.5%, N: 0.0060% or less and the balance of Fe and unavoidable impurities. The exemplary steel sheet can have thereon a galvanized layer containing, e.g., about Al: 0.05 to 10 mass % and Fe: 0.05 to 3 mass % and the balance of Zn and unavoidable impurities. Such exemplary hot dip galvanized steel sheet can have oxides containing Si in an average content of about 0.6 to 10 mass % at the crystal grain boundaries and in the crystal grains at the sheet steel side 5 μm or less from the interface between the high strength steel sheet and the plating layer and by the presence of Fe—Zn alloy with an average grain size of about 0.5 to 3 μm at the plating side.
|