LONG-FIBER-REINFORCED RESIN COMPOSITION AND MOLDED ARTICLE THEREOF |
摘要 |
A long-fiber-reinforced resin composition including the following component (A) and the component (B), the content of the component (A) being 50 to 90 wt% and the content of the component (B) being 10 to 50 wt%; and the content of reinforcing fiber contained in the component (A) being 20 to 60 wt% relative to the total amount of the fiber-reinforced resin composition:
[Component (A)]
a long-fiber-reinforced thermoplastic resin pellet including a thermoplastic resin, a modified polyolefin-based resin modified with an unsaturated carboxylic acid or its derivative and reinforcing fiber and satisfying the following (A-1) to (A-4):
(A-1): the melt index of the thermoplastic resin (resin temperature: 230°C, load: 21.18N) is 100 to 250 g/10 min;
(A-2): the relaxation time » of the thermoplastic resin at an angular frequency É=1 (rad/sec) calculated from the storage modulus G' and the loss modulus G" measured by means of a cone-and-plate rheometer is 0.1 (sec) or less;
(A-3) the content of the reinforcing fiber is 40 to 70 wt%; and
(A-4) the content of the modified polyolefin-based resin is 1 to 5 wt%;
[Component (B)]
a polyolefin-based resin satisfying the following (B-1) and (B-2):
(B-1) the melt index of the polyolefin-based resin (resin temperature: 230°C, load: 21.18N) is 20 to 70 g/10 min; and
(B-2) the relaxation time » of the polyolefin-based resin at an angular frequency É=1 (rad/sec) calculated from the storage modulus G' and the loss modulus G" measured by means of a cone-and-plate rheometer is 0.23 (sec) or less. |
申请公布号 |
EP2256150(A1) |
申请公布日期 |
2010.12.01 |
申请号 |
EP20090722098 |
申请日期 |
2009.03.19 |
申请人 |
PRIME POLYMER CO., LTD. |
发明人 |
GODA, HIROFUMI;IWASHITA, TORU |
分类号 |
C08J5/04;C08L23/02;C08L23/12 |
主分类号 |
C08J5/04 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|