The invention includes a turbine cover bucket of an alloy including carbon at less than approximately 0.04 weight percent, manganese at approximately 0.0-0.2 weight percent, silicon at approximately 0.0-0.25 weight percent, phosphorus at approximately 0.0-0.015 weight percent, sulfur at approximately 0.0-0.015 weight percent, chromium from approximately 20.0-23.0 weight percent, molybdenum from approximately 8.5-9.5 weight percent, niobium from approximately 3.25-4 weight percent, tantalum at approximately 0.0-0.05 weight percent, titanium from approximately 0.2-0.4 weight percent, aluminum from approximately 0.15-0.3 weight percent, iron from approximately 3.0-4.5 weight percent, and the remainder being nickel. The alloy is heat treated at 538° C. to 760° C. for up to 100 hours. A method of manufacturing the turbine bucket cover is also provided.
|