| 摘要 |
A stable catalyst with low volumetric shrinkage and a process for making the stable catalyst with low volumetric shrinkage is disclosed. The catalyst is made by sulfiding a catalyst precursor containing at least a Group VIB metal compound; at least a promoter metal compound selected from Group VIII, Group IIB, Group IIA, Group IVA and combinations thereof, having an oxidation state of either +2 or +4; optionally at least a ligating agent; optionally at least a diluent. In the process of making the catalyst, the catalyst precursor is first shaped then heat treated at a temperature of 50° C. to 200° C. for about 15 minutes to 12 hours, wherein the catalyst precursor still has a low (less than 12%) volumetric shrinkage after exposure to a temperature of at least 100° C.
|