A heat treatment method of manufacturing high carbon bearing steel having excellent abrasion resistance and fatigue resistance, a steel wire rod for high carbon bearing steel subjected to the heat treatment, a manufacturing method of the steel wire rod, high carbon bearing steel manufactured by the heat treatment and a soaking method of a steel bloom used for manufacturing the steel wire rod. The heat treatment method of bearings includes the steps of: quenching a bearing-shaped steel part containing, by weight, 0.5% to 1.20% carbon and 1.0% to 2.0% silicon; and partitioning the quenched steel part at a temperature ranging from Ms−100° C. to Ms for at least 10 minutes, where Ms represents a temperature at which formation of martensite will start.
|