| 摘要 |
A process is described for producing steel strips suitable for receiving a surface coating which is resisting to oxidation, in particular tin plating, of medium productivity, that does not require for its execution plants extended of a large areas or involving high economical investments. It comprises, starting from pickled hot strips having a thickness >0.7 mm, preferably obtained from thin-slab plants, a single cold rolling step by passing through not more than three stands of the Sendzimir 6Zhi type for the cold reduction of thickness to less than 0.25 mm and subsequent annealing. It is possible to obtain final thicknesses <0.18 mm both by simple reduction, which only provides subsequent skin-passing and finishing steps, and by double reduction on half-raw strip, which provides subsequent passes for thickness reduction of 30%.
|