This invention provides a bipolar plate for a fuel cell, produced by molding a composition comprising 100 parts by mass of a porous artificial graphite material having a true density of 1.63 to 2.20 g/ml and an average particle diameter (d = 50) of 20 to 100 µm, 19 to 30 parts by mass of an epoxy resin comprising a main agent and a curing agent, and 0.1 to 1.0 part by mass of an internal release agent. The main agent is an o-cresol novolak-type epoxy resin having an epoxy equivalent of 195 to 216 g/eq and an ICI viscosity of 0.20 to 1.00 Pa·s at 150°C. The curing agent is a phenol novolak resin having a hydroxyl equivalent of 103 to 106 g/eq and an ICI viscosity of 0.03 to 0.50 Pa·s at 150°C. The average thickness of a thin wall part is 0.12 to 0.20 mm. This bipolar plate is much superior in mechanical properties such as flexural strength and flexural strain and moldability to the conventional bipolar plate and, even in a reduced thickness, is satisfactorily strong and flexible and, at the same time, is also excellent in accuracy of the thickness. |