| 摘要 |
A composition for the manufacture of high strength glass fibers suitable for manufacture in a refractory lined glass melter is disclosed. The glass composition of the present invention includes 64-75 weight % SiO2, 16-24 weight % Al2O3, 8-11 weight % MgO and 0.25 to 3.0 weight % R2O where R2O is the sum of Li2O and Na2O. A composition of the present invention includes 64-75 weight % SiO2, 16-24 weight % Al2O3, 8-11 weight % MgO and 0.25 to 3.0 weight % Li2O. Another composition includes 68-69 weight percent SiO2, 20-22 weight percent Al2O3, 9-10 weight percent MgO and 1-3 weight percent Li2O. By using oxide based refractory lined furnaces the cost of production of glass fibers is substantially reduced in comparison with the cost of fibers using a platinum lined melting furnace. Fibers formed by the present invention are also disclosed. The fibers have a fiberizing temperature of less than 2650° F., a &Dgr;T of at least 80° F. Further, the glass fibers have a strength in excess of 680 KPSI, in some instances a strength in excess of about 700 KPSI, and in others a strength in excess of about 730 KPSI. The glass fibers will desirably have a modulus greater than 12.0 MPSI, in some instances greater than about 12.18 MPSI, and in certain instances greater than about 12.7 MPSI.
|