| 摘要 |
There are provided a prepreg obtained by impregnating into a fiber reinforcement a resin composition including 40 to 70 parts by weight of an aromatic bismaleimide (A) expressed by a specific general formula, 60 to 30 parts by weight of an alkenylphenol (B) expressed by a specific general formula, 1 to 10% by weight of a polyetherimide (C) of a thermoplastic resin base on the total amount of components (A) and (B), and 15 to 50% by weight of an amorphous polyimide (D) having a glass transition temperature of 200°C or higher, and a composite material obtained by heating and curing the prepreg. Also provided are the fiber-reinforced prepreg and the composite material without spoiling thermal resistance characteristic of the aromatic bismaleimide resin used as a main component of a resin and having excellent toughness imparted thereto.
|