| 摘要 |
The magnesium-contained high-silicon aluminum alloys for use as structural materials, including profiles, bars, sheets, and forgings, are manufactured by a process including the steps of: casting an alloy ingot by direct chill casting, preheating the ingot to disperse eutectic Si phase particles, and thermal-plastic processing and heat-treating to obtain the product with a final shape and a modified microstructure. The aluminum alloys contain 0.2˜2.0 wt % of Mg and 8˜18 wt % of Si, and have homogeneous and fine microstructure, wherein the aluminum matrix is equiaxed with an average grain size less than 6 μm, and the silicon and second phase particles are dispersed with an average size less than 5 μm. Without adding any modifiers, they are low-costly produced by incorporating the direct chill casting with thermal-plastic processing and heat treatment, which give rise to good plasticity and relatively high strength.
|