| 摘要 |
<P>PROBLEM TO BE SOLVED: To provide an electroconductive fiber structure having such synthetic fiber-specific properties as shapability, pliability, toughness, mechanical strength and high abrasion resistance, also having both high electroconductivity and electroconductive stability comparable to conventional metal-plated fibers, having constant electroconductivity independent of temperature/humidity change, thus having substantially invariable high electroconductivity, and slight coming off of an electroconductive agent from the fiber surface as well. Ž<P>SOLUTION: The electroconductive fiber structure is made from a resin composition containing an aromatic polyester and carbon black. The electroconductive fiber structure has a surface resistivity of 10<SP>0</SP>to 10<SP>7</SP>Ω/sq. and a density of 0.2-1.0 g/cm<SP>3</SP>. In the electroconductive fiber structure, the single filament finenesses of the electroconductive fibers forming the structure are each 0.1-20 dtex. Ž<P>COPYRIGHT: (C)2010,JPO&INPIT Ž
|