PROCESS FOR PREPARING A FABRIC CONDITIONING COMPOSITION

摘要

Fabric softening compositions with 1-10 % by weight of cationic fabric softening compound show a surprising increase in viscosity when a fatty acid partial ester of a polyhydric alcohol at a level greater than 0.01 % by weight and less than or equal to 0.45 % by weight based on the composition is added and if the resulting mixture is sheared at a temperature below the phase transition temperature of the fabric softener composition. As a result, viscosities in the range 35-500 mPa.s at 106 s-1 can be obtained in a surprising manner.