Use of an iron-chromium-aluminum alloy with long service life and minor changes in heat resistance as a foil for heating elements, the foil having a thickness ranging from 0.020 to 0.300 μm. The alloy contains (in percentages by weight) 4.5-6.5% Al and 16-24% Cr, to which are added 0.05-0.7% Si, 0.001-0.5% Mn, 0.02-0.1% Y, 0.02-0.1% Zr, 0.02-0.1% Hf, 0.003-0.020% C, maximum 0.03% N, maximum 0.01% S and maximum 0.5% Cu, the remainder being iron and the usual impurities resulting from the melting process.
|