The invention provides a high-strength steel sheet excellent in stretch-flange characteristics after working and in corrosion resistance after coating. A steel sheet which has a composition containing by mass C: 0.02 to 0.20%, Si: 0.3% or below, Mn: 0.5 to 2.5%, P: 0.06% or below, S: 0.01% or below, Al: 0.1% or below, Ti: 0.05 to 0.25%, and V: 0.05 to 0.25% with the balance consisting of Fe and unavoidable impurities and a substantially ferrite single-phase structure wherein the contents of Ti, V, and solid-soluted V in precipitates of less than 20nm in size are 200 to 1750 mass ppm, 150 to 1750 mass ppm, and 200 to less than 1750 mass ppm respectively.
|