VERFAHREN ZUR HERSTELLUNG VON ARAMIDGARN MIT HOHER FESTIGKEIT

摘要

The invention relates to a method for obtaining high-tenacity aramid yarn, wherein the yarn is made of a copolymer obtained from a mixture of monomers comprising DAPBI, an aromatic para-diamine, and an aromatic para-diacid, wherein the yarn is heated in at least two process steps, characterized in that in a first step the yarn is heated at a temperature of 200 to 360° C. at a tension of at least 0.2 cN/dtex, followed by a second step wherein the yarn is heated at a temperature of 370 to 500° C. at a tension of less than 1 cN/dtex. The invention further pertains to a multifilament aramid yarn spun from a sulfuric acid spin dope and having a tenacity of at least 2500 mN/tex.