Manufacturing method of sinter forged aluminum parts with high strength

摘要

Disclosed is a manufacturing method of sinter forged aluminum-based parts with high strength. In the manufacturing method, prepared is a raw material powder comprising, by mass: 3.0 to 10% zinc; 0.5 to 5.0% magnesium; 0.5 to 5.0% copper; inevitable amount of impurities; and the balance aluminum. The raw material powder is formed into a compact by pressing the raw material powder, sintered in a non-oxidizing atmosphere in such a manner as to heat the compact at a sintering temperature of 590 to 610 degrees C. for 10 minutes or more, before cooling the sintered compact. It is then forged by pressing the sintered compact in a pressing direction to compress the sintered compact in the pressing direction and produce plastic flow of material in a direction crossing to the pressing direction.