| 摘要 |
The present invention suggests a method of heat treatment of a Ni-based superalloy that improves resistance against creep, fatigue and stress corrosion cracking while being economical and easy, and a Ni-based superalloy produced by using the same. The method and the superalloy of the present invention include solution treatment at the high temperature region during a heat treatment process after manufacturing or final cold working fabrication. Immediately following the solution treatment, the material is slowly cooled at 1~15° C./minute down to the intermediate temperature region for aging treatment. After the slow cooling stage, aging treatment is directly performed by holding it at the intermediate temperature region for the prescribed time. Lastly, the aging treatment is followed by air-cooling stage.
|