CONVERSION OF JUST-CONTINUOUS METALLIC FILMS TO LARGE PARTICULATE SUBSTRATES FOR METAL-ENHANCED FLUORESCENCE |
摘要 |
The present invention relates to a method of producing silver films having large nanoparticles caused by cracking during anaerobic annealing to provide surfaces that exhibit increased metal enhanced fluorescence. Preferably the annealing process is conducted on a silver film having a thickness from about 14 to 17 nm for about an hour at a temperature of approximately 190°C to about 210°C resulting in the conversion of the just-continuous films into large particulate films, not readily assessable by other chemical deposition techniques. |