The present invention provides a heat-shrinkable laminated film having at least three layers including: a (I) layer; and two (II) layers respectively disposed on each surface of the (I) layer, the (I) layer being composed by a layer containing at least one polyolefin series resin as a main component and the (II) layer being composed by a layer containing at least one polylactic acid series resin as a main component, and the storage elastic modulus (E') of the laminated film at 80° C. being 10 MPa or more and 1,000 MPa or less when dynamic viscoelasticity about a direction orthogonal to the film's main shrinking direction is measured under a condition of vibrational frequency at 10 Hz, strain at 0.1%. The film of the invention exhibits excellent shrink finishing quality, heat-shrinkage property at low temperature, and small natural shrinkage; thereby suitably used for shrinkable packing, shrinkable banding packing, shrinkable label and the like.
|