A transformable lightweight structural steel, which exhibits a resistance to hydrogen embrittlement, has TRIP and TWIP properties and contains the following elements (in wt.-%): C 0.05 to <=1.0; Al 0.0 to <=11.0; Si 0.0 to <=6.0; Al+Si>0.05; Mn 9.0 to =25.0; H<20 ppm, the remainder being iron including incidental steel companion elements, whereby different phases are present depending on the alloy composition. The lightweight structural steel is characterized by associating a higher C content with a lower Mn content and associating a low C content with a higher Mn content, with the C-Mn value pairs being positioned in a C-Mn coordinate system approximately on a straight connecting line that is distant from the connecting line of the C-Mn value pairs being in balance between the austenite and martensite phases.
|