| 摘要 |
The non-settling refractory mortar of the invention contains 100 parts of ceramic powder such as cordierite, mullite, alumina, or silicon carbide, 0.5 to 1.5 parts of clay mineral, and colloidal oxide solution, in which the Ca content in total solid component is defined at 0.01 to 0.5% as converted to oxide so as to be provided with thixotropic property. As a result, the coating performance is not lowered if stored for a long period after kneading, the dimension change rate after coating is small, and cracks or gaps are not formed on the coat surface. The median diameter of ceramic powder is preferred to be 10 to 50 mum, and in order to reduce the dimension change rate after coating, the content of particles of 0.1 to 5 mum in ceramic powder is desired to be 1 to 20%.
|