MANUFACTURING METHOD OF AL-ADDED MAGNESIUM ALLOY EXTRUDED TUBE |
摘要 |
PROBLEM TO BE SOLVED: To provide a manufacturing method of an Al-added magnesium alloy extruded tube having excellent appearance and strength. SOLUTION: After the homogenization treatment of a magnesium alloy billet of 7-10 wt.% aluminum content at 350-430°C, the extrusion is performed at a billet temperature of 380-440°C, and an extrusion rate of≤1 m/min. COPYRIGHT: (C)2009,JPO&INPIT
|