| 摘要 |
<p>The present invention provides a crosslinked polyolefin-based resin-extruded foam sheet capable of reducing its thickness while retaining excellent flexibility and heat resistance. The crosslinked polyolefin-based resin foam sheet of the present invention is obtained by feeding a polyolefin-based resin and a thermally degradable blowing agent to an extruder, melting and kneading them, extruding the kneaded material through the extruder into a sheet to form an expandable polyolefin-based resin sheet, and expanding the sheet. Herein, a degree of crosslinking of the crosslinked polyolefin-based resin foam sheet is 5 to 60% by weight, an aspect ratio of a cell (MD average cell diameter/CD average cell diameter) is 0.25 to 1, and the polyolefin-based resin contains 40% by weight or more of a polyethylene-based resin obtained using a metallocene compound containing a tetravalent transition metal as a polymerization catalyst.</p> |