| 摘要 |
<p>A hot worked matrix steel consisting of (in weight-%) 0.60-0.85 C, 0.05-0.5 Si,≰0.5 (Si+Al), 0.1-2.0 Mn, 4.5-5.5 Cr, 1.5-2.6 Mo,≰1.0 W, 1.5-2.6 (Mo+W/2), 0.42-0.65 V,≰0.1 Nb,≰0.1 Ti,≰0.1 Zr,≰2.0 Co,≰2.0 Ni,≰0.003 S, optionally, up to 30 ppm B, balance iron and unavoidable impurities. The steel after hardening and tempering at 520-600° C. (2×2 h) has a hardness of 57-63 HRC and an un-notched impact energy in the transverse direction of 20-100 J. The steel consists of tempered martensite. The steel contains 1.04 vol. % or less of primary precipitated vanadium carbides. The steel is void of primary carbides other than primary precipitated vanadium carbides.</p> |