| 摘要 |
The present invention provides a method for manufacturing an ultra high strength cold-rolled steel sheet, comprising the step of continuously annealing a cold-rolled steel sheet consisting essentially of, in terms of weight percentages, 0.07 to 0.15% C, 0.7 to 2% Si, 1.8 to 3% Mn, 0.02% or less P, 0.01% or less S, 0.01 to 0.1% Sol. Al, 0.005% or less N, 0.0003 to 0.003% B, and the balance being Fe, in which such continuous annealing comprises the steps of: heating the cold-rolled steel sheet at from 800° C. to 870° C. for 10 seconds or more; slowly cooling the heated steel sheet down to from 650° C. to 750° C.; rapidly cooling the slowly cooled steel sheet down to 100° C. or less at a cooling speed of over 500° C./sec; reheating the rapidly cooled steel sheet at from 325° C. to 425° C. for from 5 minutes to 20 minutes; cooling the reheated steel sheet down to room temperature; and coiling the cooled steel sheet. According to the invention, the ultra high strength cold-rolled steel sheet, for use in a structural member of automobile, which has a tensile strength of 980 MPa or more and is excellent in stretch-flangeability, ductility, and spot-weldability can be obtained.
|