| 摘要 |
A silane-crosslinking expandable polyolefin resin composition that is flowable before foaming and composition, does not cause degassing even when foaming is carried out immediately after heat molding without the conventional crosslinking operation, and gives a crosslinked foam having superior heat resistance (heat deformation properties) after the foaming. The silane-crosslinking expandable polyolefin resin composition includes 100 parts by weight of a mixture of 5-90% by weight of a silane-grafted polyethylene resin obtained by melt mixing 100 parts by weight of LLDPE having a molecular weight distribution of 5 or less and a density of 0.87-0.945 g/cm<3>, 0.1-5 parts by weight of a vinyl-functional silane compound and 0.01-0.5 parts by weight of a free radical generator, and 95-10% by weight of a polyolefin resin; and 2-20 parts by weight of a specified organic blowing gas. |