CERAMIC GOODS FIRE CERAMIC COATING NICKEL MESH CROSSPIECE AND MAKING METHOD

摘要

A manufacturing method of ceramic coating nickel mesh supporting board for ceramic article plasticity is provided to suppress difference of contraction rate using uniform heat conduction by porosity when ceramic article is burned and to have uniform property. A manufacturing method of ceramic coating nickel mesh supporting board for ceramic article plasticity contains steps of: manufacturing nickel mesh having 20~40mm lattice typed porosity(4) using nickel; ultrasonic-cleaning the nickel mesh and performing grids blasting; plasma spraying zirconia(Zr2O3) ceramic powder including yttria(Y2O3) of weight ratio 2~10% on a surface of the nickel mesh; forming a ceramic coating layer having 50~100 mu of thickness by welding the ceramic coating layer at high temperature of 2500~3000°C; and manufacturing ceramic coating nickel mesh supporting board(1) for the ceramic article plasticity.