A method for producing a welded rotor of a low-pressure steam turbine, the method including providing a first forging including a steel with a minimum yield strength of approximately 700 Mpa. A second forging is provided including a heat-treated 3.5 NiCrMoV stel having an average chemical composition of 3.5% of Ni, 1.5% of Cr, 0.35% of Mo, 0.10% of V, 0.25% of C, remainder Fe. A build-up layer of welding deposit is applied to a connection surface of the second forging using build-up welding. A first local post-weld stress-relief annealing is performed so as to soften the build-up layer and a corresponding heat-affected zone. The first and second forgings are joined together so as to provide a welding location. The welding location is filled using a welding deposit so as to provided a welded join. The welded join is subjected to a second post-weld stress-relief anneal.
|