| 摘要 |
<p>A method of producing blister copper from raw material containing antimony. The invention is characterized in that a slag is separated from copper matte formed by smelting the raw material. Thereafter the matte is brought into contact, under violent agitation preferably in a rotary converter of the Kaldo type, with a substantially inert gas in a quantity sufficient to reduce by volatilization the antimony content of the copper matte and, possibly, also the content of other impurities such as bismuth, arsenic and zinc to a level acceptable when performing the subsequent converting process, so as to obtain the desired blister copper product, preferably a maximum content of antimony, 0.04 percent by weight and of bismuth 0.03 percent by weight, The rotary converter is suitably operated with a rotation corresponding to a peripheral speed of approximately 0,5 - 7 m/s, preferably 2-5 m/s.</p> |