PURPOSE:To obtain the titled synthetic leather able to be wrinkled, by applying a polyether polyurethane having a specific modulus to a fiber texture of a woven or knit fabric, etc., coagulating the polyurethane and laminating a specific binder coat and a top-coat to the substrate layer. CONSTITUTION:A polyether polyurethane containing polypropylene glycol as a polyol component and having a 100% modulus of 150-400kg/cm<2> is applied to a fiber texture of a woven or knit fabric, etc., and coagulated to obtain a fibrous substrate layer. Separately, a binder coat composed of a polyether polyurethane containing polytetramethylene glycol as a polyol component and having a 100% modulus of 15-50kg/cm<2> is laminated on a top-coat composed of a polycarbonate polyester polyurethane having a 100% modulus of 200-600kg/cm<2> with yield value. The above microporous substrate is hot-pressed to the surface of the laminate and the product is crumpled to obtain the objective wrinkled synthetic leather.
|