Production method of expansion-molded article of polypropylene resin

摘要

An expansion-molded article of a polypropylene resin is produced by filling pre-foamed particles of the polypropylene resin, which have a crystalline structure featuring an inherent peak inherent to the polypropylene resin and a high-temperature peak on the temperature side higher than the temperature corresponding to the inherent peak on a DSC curve obtained by differential scanning calorimetry of the pre-foamed particles and a bulk density of 0.04 g/cm3 or higher and require melting energy of 8-12 J/g at the high-temperature peak, in a mold without applying any pretreatment to the pre-foamed particles to build up an internal pressure therein, and then heating the pre-foamed particles, whereby the pre-foamed particles are caused to expand into the expansion-molded article conforming with the mold. The pre-foamed particles may alternatively have a bulk density lower than 0.04 g/cm3 and require melting energy of at least 8 J/g.