| 摘要 |
The invention provides a poly(trimethylene terephthalate) drawn yarn pirn. The drawn yarn pirn of the invention comprises poly(trimethylene terephthalate) drawn yarn having an intrinsic viscosity of 0.7-1.3 dl/g, a heat shrinkage stress-exhibiting initial temperature of 55 DEG C or higher, a heat shrinkage stress extreme temperature of 150-190 DEG C and a breaking elongation of 36-60%, wound at a wound hardness of 80-90. The drawn yarn pirn of the invention exhibits satisfactory reelability even with high-speed false twisting, as well as minimal yarn breakage and fluff generation, thereby giving a textured yarn with satisfactory quality. <IMAGE> |