摘要 |
<p>A multi-filament poly(trimethylene terephthalate) yarn is provided. The poly(trimethylene terephthalate) yarn has a crystal orientation function of at least 0.6 and an elongation at break of between 65% and 110%. A process for producing the yarn is also provided in which poly(triemethylene terephthalate) is melt-spun into a multi-filament yarn, the yarn is cooled to a yarn temperature of less than 50° C., and the cooled yarn is taken-up at a take-up speed of at least 3500 m/min while maintaining the temperature of the yarn at a yarn temperature of less than 50° C.</p> |