| 摘要 |
The invention provides an olefin resin composition for powder molding comprising 100 parts by weight of an olefin resin (A) having a glass transition temperature of 25 DEG C or lower such as a propylene homopolymer or hydrogenated styrene-butadiene block copolymer and 0.5 to 30 parts by weight of a non-halogen type thermoplastic resin (B) such as methyl methacrylate having a glass transition temperature of 60 to 200 DEG C, an average particle diameter of 0.1 to 10 mu m and a sphericity of 0.8 to 1.0. The resin composition is very excellent in powder flowability and can be easily molten even under conditions where there is little or no pressure or shear stress action, and so best suited for use as powder slush molding compositions. |