A magnetic powder composed primarily of Fe that has been surface-treated with a silane coupling agent, which magnetic powder is characterized in that it contains Co such that Co/Fe expressed in atomic percent is 20-50 at. %, Al such that Al/Fe expressed in atomic percent is 5-30 at. %, and one or more rare earth elements R (including Y) such that R/Fe expressed in atomic percent is 4-20 at. %, and has average particle diameter of smaller than 80 nm, TAP density of 0.7 g/cm<SUP>3 </SUP>or greater, ignition point of 165° C. or higher, and oxygen content of 26 wt % or less.
|