| 摘要 |
A nickel-base superalloy article, such as a gas turbine stationary flowpath shroud that has previously been in service, is repaired by applying a restoration coating to a surface of the article. The restoration coating is applied by providing a precursor mixture, wherein the precursor mixture has no more than about 15 weight percent chromium and no more than about 0.01 percent yttrium, and wherein the precursor mixture includes a higher-melting-point alloy component and a lower-melting-point alloy component. The precursor mixture is applied to the surface of the article, in a form such as a preform of the alloy components. The article with the precursor mixture applied to the surface thereof is heated to a sufficiently high temperature to melt the lower-melting-point alloy component, thereby forming the restoration coating on the surface of the article. |