| 摘要 |
Disclosed are a thermoplastic resin composition capable of being processed stably into a thin article (e.g., a film, a sheet, a bag) by extrusion molding such as calendar molding and also capable of providing a thin article or the like in which an undesirable phenomenon caused by the generation of a flow mark on the surface is improved and which shows an excellent blush resistance upon being bent; a process for producing the composition; a molded article; and an article comprising the molded article. The thermoplastic resin comprises an acrylic rubbery polymer-reinforced resin having a graft ratio of 80 to 170%. In the resin, the acrylic rubbery polymer has a number average particle diameter of 60 to 150 nm, the acetonitrile-soluble fraction of the resin has a limiting viscosity of 0.4 to 0.8 dl/g and a content of the bound vinyl cyanide compound of 20 to 30% by mass, and the standard deviation of the distribution of the content of the bound vinyl cyanide compound as measured by liquid chromatography is 5 or less. ® KIPO & WIPO 2008
|