| 摘要 |
<P>PROBLEM TO BE SOLVED: To provide a ceramic composite having excellent characteristics and capable of being economically formed into a profile such as a cylinder, a honeycomb and a corrugated article, further enabling a third functional material to be supported in pores since a size of the pores is controllable when it is molded into a porous article or the like, and a ceramic molded article. <P>SOLUTION: The ceramic composite comprises 1-30 pts.wt of a resin constituent (A), 99-70 pts.wt. of a ceramic constituent (B), and 50-300 pts.wt. of a plasticizer (C) based on 100 pts.wt. of a total weight of (A) and (B), wherein the resin constituent (A) contains a polyolefine having a viscosity average molecular weight Mv of not less than 600,000, the relationship between a content W(A) pts.wt. of the resin constituent (A) and a viscosity average molecular weight Mv(A) of the resin constituent (A) satisfies expression (1): W(A)×Mv(A)/1,000,000 ≥7 (1), and the average particle size of the ceramic constituent (B) is 0.005-10 μm. <P>COPYRIGHT: (C)2008,JPO&INPIT |