| 摘要 |
PROBLEM TO BE SOLVED: To provide an extrusion product having excellent transparency and good balance between strength and molding processability. SOLUTION: The transparent extrusion product is obtained by extruding a resin composition composed of 1-90 wt.% of a copolymer (A) composed of 1-10 wt.% of an alkyl (meth)acrylate-based monomer having 25-60 cm<SP>3</SP>/10 min MVR (melt volume rate) (measured under conditions of 220°C and 10 kg according to ISO 1133) and 99-90 wt.% of an aromatic vinylic monomer and 99-10 wt.% of a polycarbonate resin (B) having≤3 cm<SP>3</SP>/10 min MVR. COPYRIGHT: (C)2008,JPO&INPIT
|