摘要 |
<p>A method of preparing a carbon solid using tar sludge obtained from a coke manufacturing process is provided to create efficient and high-value usage of the tar sludge, and to manufacture the carbon solid by a simple treatment without adding additionally aggregate. A method of preparing a carbon solid includes the steps of: pulverizing a solid content in a tar sludge, and blowing in air therein at 350-450deg.C for 30min to 1hour, so as to obtain a self-sinterable powder of 0.1mm in size; press-forming the powder under 100-2000kg/ cm^2, and firing the powder at 800-1000deg.C for 30min to 1 hour under inert atmosphere using argon or nitrogen gas. The solid content is mostly composed of fine cokes and a little of fine coal particles, and has an average particle size of 0.5mm or less.</p> |