BASE FABRIC FOR CHEMICAL LACE AND PROCESS FOR PRODUCTION THEREOF

摘要

A base fabric for producing chemical lace of the present invention is fabricated from dyed embroidery yarn and nonwoven fabric formed of a water-soluble poly (vinyl alcohol)-based fiber random web, which base fabric satisfies the following conditions: (1) a binder to be adhered onto the nonwoven fabric is formed of a foamy aqueous solution containing a poly (vinyl alcohol)-based resin, and the binder is deposited onto the nonwoven fabric in an amount of 2 to 20 mass% with respect to the total mass of the nonwoven fabric; (2) the nonwoven fabric has a 10% modulus strength in the widthwise direction of 15 to 80 N/50·mm width; and (3) the nonwoven fabric has a bending resistance of 40 to 150 mm. The base fabric for producing chemical lace is soft and easy to handle, has high dimensional stability and low dissolution temperature, prevents skips and non-uniformity in embroidery motifs, and is produced at low cost.