| 摘要 |
A method of adhering composite of ceramic particles to a surface of an orthodontic bracket that has a base portion for attachment to a tooth is provided. The particles are comprised of products of reaction of molten aluminum hydroxide, hydroxyapatate (calcium phosphate hydroxide), and alumina in an inert atmosphere. Average particle size of aluminum powder and hydroxyapatate powder is 30 micrometer. Mixture of nanometer and micrometer alumina is used. Aluminum hydroxide powder and other materials which are provided in dry powder form is dispersed in a high viscosity mineral oil. Molten aluminum hydroxide at 300° C. holds the other particles in place and reacts with hydroxyapatate to produce complex of aluminum phosphate and calcium hydroxide. Programmed heat treatment produce an orthodontic bracket having an opaque base portion for attachment to a tooth that shows bond strength of 180 kg/cm<SUP>2 </SUP>though the maximum temperature of heat treatment is lower than 1,000° C.
|