<p>This bake-hardening hot-rolled steel sheet with excellent workability, contains, in terms of mass %, C of 0.01 to 0.2%, Si of 0.01 to 2%, Mn of 0.1 to 2%, P of 0.1 % or less, S of 0.03% or less, Al of 0.001 to 0.1%, N of 0.01% or less, Nb of 0.005 to 0.05%, and as the remainder, Fe and unavoidable impurities, wherein the microstructure is a polygonal ferrite and/or a continuous-cooled microstructure having an average particle diameter of 2 µm to 8 µm, and the grain boundary abundance ratio of solute C and/or solute N is 0.28 or lower. This method for manufacturing a hot-rolled steel sheet includes: heating a slab containing aforementioned components to at least a temperature satisfying the equation of SRT (°C) = 6670/{2.26 - log(%Nb)(%C)} - 273 (A); subjecting the heated slab to a rough rolling, a finish rolling under a condition where the final temperature is in a range of the Ar 3 transformation point temperature or higher and (Ar 3 transformation point temperature + 100°C) or lower; cooling it at a cooling rate of 80°C/sec or higher from cooling initiation down to a temperature range of 500°C or lower; and coiling it.</p> |