| 摘要 |
Glass is produced by depositing presintering composition on a preform set into move in front of a plasma torch which moves back and forth substantially parallel to a longitudinal direction of the preform, a first feed duct feeds the plasma with grains of the presintering composition while optionally a second feed duct feeds the plasma with a fluorine or chlorine compound, preferably a fluorine compound, mixed with a carrier gas, whereby the presintering composition consists of granules of metal oxides or metalloid oxides of a pyrogenic silicon dioxide powder with a BET surface area of 30 to 90 m^2/g, a DBP index of 80 or less, a mean aggregate area of less than 25000 nm^2 and a mean aggregate circumference of less than 1000 nm, wherein at least 70% of the aggregates have a circumference of less than 1300 nm or a high-purity pyrogenically prepared silicon dioxide having metal contents of less than 0.2 Vg/g, which is prepared by reacting a silicon tetrachloride having a metal content of less than 30 ppb by means of flame hydrolysis.
|