This invention relates to an aluminum titanate body having a narrow pore size distribution as characterized by the relation (d<SUB>50</SUB>-d<SUB>10</SUB>)/d<SUB>50 </SUB>being less than 0.50 corresponding to a high degree of interconnected porosity. The body also preferably exhibits a low coefficient of thermal expansion of less than 15x10<SUP>-7 </SUP>C<SUP>-1</SUP>, high porosity of at least 38% by volume, and at least 0.10% by weight metal oxide, the metal being either yttrium, calcium, bismuth, a lanthanide metal or combinations of thereof. MOR is preferably at least 450 psi. Median pore diameter is preferably at least 8 microns. The inventive ceramic body is particularly useful as a wall-flow filter for a diesel exhaust. A method of fabrication is provided where the sintering temperature is preferably between 1375°-1550° C.
|