| 摘要 |
1,024,799. Moderators. UNITED STATES ATOMIC ENERGY COMMISSION. Aug. 17, 1964 [Oct. 28, 1963], No. 33491/64. Heading G6C. [Also in Division B3] A method of welding a graphite-to-graphite interface comprises the steps of exerting an initial pressure of about 14,000 p.s.i. across the interface and while continuing said initial pressure, passing an alternating current having a peak current density of from 310,000 to 1,000,000 amps/sq. in. across said interface, while simultaneously exerting a second pressure of such magnitude that the total pressure shall equal about 15,000 p.s.i. across the entire interface as enlarged by the resistance heating effect of the current. An apparatus for carrying out the method to seal a nuclear reactor fuel container made of nuclear graphite comprises a frame 11 having upward projections 12, 13, 14. The stator 15 of an electromagnet is mounted on the projection 14 and has an armature 19 mounted on a shaft 18 which also carries at one end the piston 22 of a pneumatic cylinder 21. At the other end of the shaft is mounted a chuck 30 which is insulated from the shaft 18 and which receives the conical end 32, Fig. 2 (not shown) of a high-purity graphite plug which forms one of the workpieces. The other workpiece is a high-purity graphite tube 33 which is located axially by an insulated end-stop 40 and positioned radially by an insulated holderelectrode 41 made of copper alloyed with tungsten or tungsten-carbide and having an insert 42 of even greater heat resistivity. The cuhck 30 which is also an electrode is made of the same material as the electrode 41. The welding current circuit comprises the secondary of a transformer 45, the lead 44, the stator 15, the lead 34, the electrodes and workpieces and a return lead to the transformer. Operation.-The initial pressure between the workpieces is created by the pneumatic cylinder 21 and the additional pressure by the attraction of the armature 19 by the stator 15 which is energized by the welding current. In an example in which the apparatus was enclosed in a vessel evacuated to 25 microns of Hg to avoid bubble formation the tube 33 had an outside diameter of 0À551 inch and a wall thickness of 0À030 inch. The interface between the tube and the plug was conical. The initial pressure was 14,000 p.s.i. and a one-cycle pulse lasting 16À6 milliseconds was passed, producing a peak current density of 310,000 amps/sq. inch. The interfacial area enlarged by four times and the final interfacial pressure was 1500 p.s.i. A second example describes the welding of two parts each consisting of a solid graphite rod, the meeting ends being tapered to 1/8 inch diameter.
|