The present invention provides a cast steel for ring-shaped components that has a low average coefficient of thermal expansion in a temperature range of 20 DEG C to 500 DEG C and high strength and good oxidation resistance at 500 DEG C, which are required for ring-shaped components for use as blade rings and seal ring retainers of gas turbines, and that can hence be used for blade rings and seal ring retainers of gas turbines. Specifically, the present invention provides a high-strength and low-thermal expansion cast steel comprising, on a mass percentage basis, 0.1 to 0.8% of C, 0.1 to 1.0% of Si, 0.1 to 1.0% of Mn, 0.01 to 0.1% of S, greater than 40% and up to 50% of Ni, not greater than 4% (inclusive of 0%) of Co, greater than 1.5% and up to 4% of Cr, 0.01 to 0.1% of Al, and 0.001 to 0.1% of Mg, the remainder being substantially Fe. |