HIGH STRENGTH SPRING AND METHOD FOR MANUFACTURE THEREOF

摘要

A high strength spring steel of this invention is characterized in containing, in percent of mass, of C: 0.36-0.48%; Si: 1.80-2.80%; Mn: 0.20-1.40%; P: 0.015% or less; S: 0.010% or less; Cu: 0.10-0.50%; Ni: 0.10-2.00%; Cr: 0.05-1.20%; s-Al: 0.005-0.040%; N: 0.002-0.012%; O: 0.002% or less, while the remainder is constituted of Fe and inevitable impurities and the quantity of inclusions of 10 mum or larger in diameter per field of vision of 100 mm² is 10 or less. A manufacturing method of high strength spring of this invention is characterized in that the high strength spring steel which is tempered to HRC52 or higher is formed into a spring shape by hot forming or cold forming and warm shot peening is carried out so as to produce a high strength spring of 1176 MPa or higher in maximum shearing stress.